Vsebina Ferro Niobuima
Pustite sporočilo
Vsebina pf Ferro Niobuim
|
Ocena |
sestava ％ | |||||||||||||||
| Nb | Ta | Al | Si | C | S | P | W | Ti | Cu | Mn | Kot | Sn | Sb | Pb | Bi | |
| Manj ali enako | ||||||||||||||||
| FeNb70 | 70-80 | 0.8 | 3.8 | 1.5 | 0.04 | 0.03 | 0.04 | 0.3 | 0.3 | 0.3 | 0.3 | 0.005 | 0.002 | 0.002 | 0.002 | 0.002 |
| FeNb60—A | 60-70 | 0.5 | 2.0 | 0.4 | 0.04 | 0.02 | 0.02 | 0.2 | 0.2 | 0.3 | 0.3 | 0.005 | 0.002 | 0.002 | 0.002 | 0.002 |
| FeNb60—B | 60-70 | 0.8 | 2.0 | 1.0 | 0.05 | 0.03 | 0.05 | 0.2 | 0.3 | 0.3 | 0.3 | 0.005 | 0.002 | 0.002 | 0.002 | 0.002 |
| FeNb50—A | 50-60 | 0.8 | 2.0 | 1.2 | 0.05 | 0.03 | 0.05 | 0.1 | 0.3 | 0.3 | 0.3 | 0.005 | 0.002 | 0.002 | 0.002 | 0.002 |
| FeNb50—B | 50-60 | 1.5 | 2.0 | 4.0 | 0.05 | 0.03 | 0.05 | |||||||||
Fero niobijje dodana snov v postopku ustvarjanja nejasnih kovin in bo naslednji spojini dala nekaj privlačnih lastnosti. Ena bistvenih prednosti dodajanjaFero niobijamalgamu je njegov sovražnik destruktivnih lastnosti (boljši od vsega ogljikovega jekla). Poleg tega lahko dodajanje fero niobija kombinaciji naredi vse bolj varljivo in veliko bolj ozemljeno. Z razširitvijo različnih komponent, na primer cirkonija, jekla, ustvarjenega s fero niobijem, so idealne za usmerjeno občutljive aplikacije, na primer razpone obes. Fero niobij poveča visokotemperaturno nasprotje, oviro pri porabi, oviro oksidacije, nasprotovanje lezenju, tako kot zmanjša razpad pri višjih temperaturah.
ZHEN AN INTERNATIONAL CO., LTD
Mobilni: +86-18211636583(whatsapp/wechat)
Faks: +86-372-5055180
Email:kay@zaferroalloy.com
Spletna stran: https://www.zaferroalloy.cn/
Sedež: pisarna Huafu, mesto Anyang, provinca Henan, Kitajska